LNP™ LUBRICOMP™ UX96507 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4DRMtF_LNP-LUBRICOMP-UX96507-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UX96507 is a compound based on PPA containing proprietary fillers. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-U-96507 Product reorder name: UX96507 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.50 | g/cm³ | |
| -- | 1.49 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.010 to 0.030 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.29 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19300 | MPa | ASTM D638 |
| -- | 18700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 226 | MPa | ASTM D638 |
| Break | 226 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 16900 | MPa | ASTM D790 |
| -- 5 | 16800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 313 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 311 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 74 | J/m | ASTM D256 |
| 23°C 7 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 8 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.00 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 280 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 277 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 262 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 259 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.2E-6 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 to 327 | °C | |
| Middle Temperature | 327 to 338 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 321 to 349 | °C | |
| Mold Temperature | 48.9 to 104 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/ABS-G10 | Polymer Resources Ltd. | PC+ABS | PRL |
| Sarlink® TPE ML-1660B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| NOVALAC FM 4004 | Vyncolit N.V. | Phenolic | NOVALAC |
| Fainplast PVC CKL 87/5 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fiberfil® J-60/40/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |