NORYL GTX™ GTX840 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4CGDsy_NORYLGTXGTX840resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% glass filled PPE+PA66 blend for automotive under-the-hood and FLEN applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.24 - 0.27 | % | Internal method |
| Transverse flow : 3.20mm | 0.60 - 0.63 | % | Internal method |
| Water Absorption | |||
| Equilibrium, 23°C | 0.30 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13500 | MPa | ASTM D638 |
| -- | 13900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 178 | MPa | ASTM D638 |
| Fracture | 198 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 11900 | MPa | ASTM D790 |
| -- 5 | 12300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 280 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 249 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 11 | kJ/m² | ISO 179/2C |
| 23°C 7 | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 94 | J/m | ASTM D256 |
| -30°C 8 | 11 | kJ/m² | ISO 180/1A |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 260 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.40mm | 247 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 244 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 246 | °C | ISO 306/B50, ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.6E-5 - 2.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.0E-5 - 9.4E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 277 - 316 | °C | |
| Middle Temperature | 282 - 316 | °C | |
| Front Temperature | 288 - 316 | °C | |
| Nozzle Temperature | 293 - 316 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 76.7 - 121 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: .02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 4112 | Teknor Apex Company | PVC, Flexible | APEX® |
| Ferro PP TPP10AN52NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Edgetek™ AS-000/000 AS NC505 | PolyOne Corporation | ABS | Edgetek™ |
| ESTOPLAST XU 64001NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| LUVOCOM® 1800-8567 | LEHVOSS Group | PET | LUVOCOM® |