MXSTEN® CV77516
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | MXSTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4C9A28_MXSTEN-CV77516.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mxsten CV Plastomer CV77516 resin is a polyethylene plastomer designed for blown film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness and high melting point. Application/Uses ?- Blown film ?- Food Packaging |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 56.5 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 44.1 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 750 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1100 | % | ASTM D882 |
| Dart Drop Impact 3(25 µm, Blown Film) | 1700 | g | ASTM D1709A |
| Seal Initiation Temperature 4(25 µm, Blown Film) | 88.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 425° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 4121 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Axiall PVC 18640 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Comtrex Flexible PVC® 63XCF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| Fainplast PVC PG 55/A | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| LEXAN™ 221R resin | SABIC Innovative Plastics | PC | LEXAN™ |