SCHULAMID® 66 GF 30 FR 2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4C97Ir_SCHULAMID-66-GF-30-FR-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced flame-retardant Polyamide 66 grade; halogen free |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 155 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 250 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 242 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | > 250 | °C | ISO 306/A50 |
| -- | 229 | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 0.750 mm, Self-Extinguishing | 0.0 | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | mm/min | |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 750 | °C | |
| 1.50 mm | 750 | °C | |
| 3.00 mm | 750 | °C | |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hax™ CAT 103 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Karina MBPEB WHITE E- 1000/1075 - IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumid® SG4389B | LG Chem Ltd. | Nylon 66 | Lumid® |
| ESTOPLAST XU 150BL13 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |
| LEXAN™ OQ4120R resin | SABIC Innovative Plastics | PC | LEXAN™ |