Geon™ Vinyl Rigid Extrusion 87566
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4C3FzU_GeonVinylRigidExtrusion87566.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon™Vinyl Rigid Extrusion 87566 is a rigid polyvinyl chloride product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2550 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 49.6 | MPa | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 130 | J/m | ASTM D256A |
| Drop Impact Resistance | 51.4 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, annealed, 3.18mm 3 | 71.1 | °C | ASTM D648A |
| 0.45 MPa, annealed, 3.18mm 4 | 74.3 | °C | ASTM D648A |
| 1.8 MPa, annealing, 3.18mm, injection molding 5 | 69.1 | °C | ASTM D648A |
| 1.8 MPa, annealing, 3.18mm, injection molding 6 | 72.2 | °C | ASTM D648A |
| CLTE - Flow (-30 to 30°C, mm) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Annealed at 122 degree F (50 degree C) |
| 4 . | Annealed at 140 degree F (60 degree C) |
| 5 . | Annealed at 122 degree F (50 degree C) |
| 6 . | Annealed at 140 degree F (60 degree C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tefzel® 280 | DuPont Fluoropolymers | ETFE | Tefzel® |
| Capilene® QW 80 AV | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| FERREX® GPP20CF21HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| POLYfill PPC T1035 | Polykemi AB | PP Copolymer | POLYfill |
| Sylvin 8445-70 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |