PLEXIGLAS® 8N is an amorphous thermoplastic molding compound (PMMA).

Typical properties of PLEXIGLAS® molding compounds are:

good flow

high mechanical strength, surface hardness and abrasion resistance

high light transmission

very good weather resistance

free colorability due to crystal clarity

Special properties of PLEXIGLAS® 8N are:

optimum mechanical properties

maximum heat deflection temperature

good flow / melt viscosity

AMECA listing.

Application:
Used for injection molding optical and technical items.

Examples:
optical waveguides, luminaire covers, automotive lighting, instrument cluster covers, optical lenses, displays, etc.

General Information
Features	Amorphous Good Abrasion Resistance Good Colorability Good Flow Good Weather Resistance High Hardness High Strength
Uses	Automotive Applications Automotive Backlights Displays Lenses Optical Applications Protective Coverings
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	3.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	77.0	MPa	ISO 527-2/5
Tensile Strain (Break)	5.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	98.0	°C	ISO 75-2/A
Glass Transition Temperature	117	°C	ISO 11357-2
Vicat Softening Temperature	108	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2
Haze	< 0.50	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	< 98.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	60.0 to 90.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
MarFlex® 5335	Chevron Phillips Chemical Company LLC	LDPE	MarFlex®
THERMOLAST® K TC7TPZ (Series: GP/AP)	KRAIBURG TPE	TPE	THERMOLAST® K
Colorite 66 Series 1066	Colorite Polymers	PVC, Unspecified	Colorite 66 Series
Lupoy® EF5001RFT	LG Chem Ltd.	PC+ABS	Lupoy®
Sylvin 4200-85 Brown 7440	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin