The matrix plastic of Kareline® ABMS is Acrylonitrile-butadiene-styrene (ABS). The fibre used is ECF bleached long fibre Nordic soft wood pulp (cellulose). The fibre content of Kareline® ABMS composites is normally 10 - 30 weight% (for example Kareline® ABMS7030). Customer tailor-made grades, e.g. with higher fibre content, are available. Injection mouldable Kareline® ABMS composites can be used in various products because of its good balance of properties, toughness/strength/temperature resistance coupled with its ease of moulding and good surface finish. Kareline® ABMS composites are excellent raw materials for technical applications e.g. in car, telecom or electronics industries, covers, handles, but also for household appliances, decorative parts, furniture and interior design. If needed, it is possible to have Kareline® ABMS products with very beautiful and living surface structure and colours. Kareline® ABMS composites have a lot of good properties: High rigidity Good impact strength as natural fibre composite Excellent abrasion resistance Good chemical and stress cracking resistance Easy to machine Pleasant feel of surface and good surface quality; if needed very beautiful living/natural surface is possible Good acoustic properties Problem-free surface treatment

Message

The matrix plastic of Kareline® ABMS is Acrylonitrile-butadiene-styrene (ABS). The fibre used is ECF bleached long fibre Nordic soft wood pulp (cellulose). The fibre content of Kareline® ABMS composites is normally 10 - 30 weight% (for example Kareline® ABMS7030). Customer tailor-made grades, e.g. with higher fibre content, are available.

Injection mouldable Kareline® ABMS composites can be used in various products because of its good balance of properties, toughness/strength/temperature resistance coupled with its ease of moulding and good surface finish.

Kareline® ABMS composites are excellent raw materials for technical applications e.g. in car, telecom or electronics industries, covers, handles, but also for household appliances, decorative parts, furniture and interior design. If needed, it is possible to have Kareline® ABMS products with very beautiful and living surface structure and colours.

Kareline® ABMS composites have a lot of good properties:

High rigidity

Good impact strength as natural fibre composite

Excellent abrasion resistance

Good chemical and stress cracking resistance

Easy to machine

Pleasant feel of surface and good surface quality; if needed very beautiful living/natural surface is possible

Good acoustic properties

Problem-free surface treatment

General Information
Filler / Reinforcement	Wood Fiber
Features	Electrically Insulating Food Contact Acceptable Good Abrasion Resistance Good Chemical Resistance Good Dimensional Stability Good Impact Resistance Good Moldability Good Surface Finish Good Weather Resistance High ESCR (Stress Crack Resist.) High Rigidity Laser Markable Machinable Paintable Renewable Resource Content Thermally Insulating Ultrasonic Weldable
Uses	Appliances Automotive Applications Decorative Parts Electrical/Electronic Applications Furniture Handles Household Goods Protective Coverings Simulated Wood Parts Telecommunications
Appearance	Brown
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (200°C/10.0 kg)	1.50	cm³/10min	ISO 1133
Molding Shrinkage	0.50	%

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 23°C)	80		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2
Tensile Stress (Yield)	49.5	MPa	ISO 527-2
Tensile Strain (Yield)	2.7	%	ISO 527-2
Flexural Modulus	4800	MPa	ISO 178
Tensile Strength/Weight Ratio	42.0	MPa/g/cm³

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.8	kJ/m²	ISO 179

Thermal	Nominal Value	Unit
Continuous Use Temperature	-30.0 to 100	°C

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0 to 100	°C
Drying Time	4.0 to 8.0	hr
Rear Temperature	180	°C
Middle Temperature	190	°C
Front Temperature	195	°C
Nozzle Temperature	200	°C
Processing (Melt) Temp	< 210	°C
Mold Temperature	20.0 to 50.0	°C
Injection Pressure	< 100	MPa

Resin Grade	Manufacturer	Category	Trademark
Romiloy® 6020	ROMIRA GmbH	ASA+PC	Romiloy®
RTP 200 UV	RTP Company	Nylon 66	RTP
Polymer-E F8101	Asia Polymer Corporation (APC)	LDPE	Polymer-E
ResMart ABS VH-0800 Black	ResMart	ABS	ResMart
TECHNYL STAR® S 60G1 V30 GREY R7016 CF	Solvay Engineering Plastics	Nylon 6	TECHNYL STAR®

Resin Grade

Manufacturer