Syncure™ GR150
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4BSMrt_SyncureGR150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Graft Resin component for PolyOne's Syncure™ system, which is a two-step, silane-grafted, moisture-crosslinkable polyethylene system. Graft Resins have approximate shelf life of 6 months from the date of production. Please consult PolyOne for its use past 6 months. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Apparent Density 1 | 0.50 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 0.39 | g/10 min | ASTM D1238 |
| Gel Content 3 | 75 | % | ASTM D2765 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 4(131°C) | 3.6 | % | UL 1581 |
| Thermal creep elongation 5 | 35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 6 | 11.0 | MPa | ASTM D638 |
| Tensile Strength 7(Break) | 16.5 | MPa | ASTM D638 |
| Tensile Elongation 8(Break) | 600 | % | ASTM D638 |
| Additional Information |
|---|
| 张力、伸长率、变形值、热蠕变和凝胶值基于95 phr S1060A / 5 phr S1000B系统测量得出；并在90摄氏度的水中硫化6小时。颗粒外观为 1/8"圆柱状。 |
| Note Message | |
|---|---|
| 1 . | Geon® 1169 |
| 2 . | Procedure A |
| 3 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 4 . | 500g,1 hour |
| 5 . | SYV-40 |
| 6 . | Type 4, 510mm/min |
| 7 . | Type 4, 510mm/min |
| 8 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ XP6042701 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Daelim Po1y® PR-780B | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Ferro PP TPP20AD82UL NATURAL | Ferro Corporation | PP Homopolymer | Ferro PP |
| ESENTTIA 07R87 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Honghai CM 352L | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |