Hostacom HYP 376D NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Af3wk_HostacomHYP376DNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom HYP 376D NAT is an over 40% chalk filled PP homopolymer, with good detergent resistance, very good mouldability and high flowability. Please contact Basell for shrinkage recommendations. This grade is not intended for medical, pharmaceutical, food, drinking water and all applications not listed in the supported list. For more information please contact our sales representatives. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.29 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 28.0 | cm³/10min | ISO 1133 |
| Ash Content (500°C) | 45.5 | wt% | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2800 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 2.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 24 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XENOY™ X5230 resin | SABIC Innovative Plastics Europe | PC+PET | XENOY™ |
| China PPS hGR40 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Geon™ Vinyl Flexible A85U1 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina IVORY PVC COMPOUND -E 655-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pinnacle PP 6199C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |