Trithene®TS 4016 is a low density polyethylene LLDPE material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TS 4016 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.10 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 100 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 110 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 460 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 780 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 350 | g | ASTM D1922 |
| TD : 50 µm, blown film | 530 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, 50.0 µm, blown film | 63 | ASTM D2457 | |
| 60, 50.0 µm, blown film | 96 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Teor de Linear, PTN-736-Q: 22.5% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 165 | °C | |
| Cylinder Zone 2 Temp. | 170 - 175 | °C | |
| Cylinder Zone 3 Temp. | 170 - 180 | °C | |
| Adapter Temperature | 175 - 185 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 233 GH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Ferro PP LPP40BD26WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| MAGNUM™ 3416 SC | Trinseo | ABS | MAGNUM™ |
| Plenco 08218 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |
| LNP™ THERMOCOMP™ IX04513C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |