Chemlon® N60A
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 48cIwx_Chemlon-N60A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N60A is a general purpose, unfilled, nucleated and lubricated injection moulding grade of nylon 6. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.2 - 2.0 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 68.0 | 36.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2900 | 800 | MPa | ISO 178 |
| Flexural Stress 2 | 80.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 14 | 10 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.60 | 4.20 | IEC 60250 | |
| Comparative Tracking Index | > 600 | > 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (1.50 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| Back pressure: LowInjection pressure: MediumNo drying is necessary unless the materials has been exposed to air for longer than three hours. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | At conventional deflection |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TPE D4107 C | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Ebalta MG 453 GF / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| K-Prene GHT 65 | Technovinyl Polymers India Ltd. | TPE | K-Prene |
| Jampilen HP527J | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Petrotene® PP A3 G40 PRTA011 PH366 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |