LNP™ LUBRICOMP™ DL003E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 48OoEz_LNPLUBRICOMPDL003Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Easy Molding. Also known as: LNP* LUBRICOMP* Compound DL-4030 EM Product reorder name: DL003E |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.80 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2190 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.1 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Fracture | 50.3 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.6 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2 |
| Fracture | 26 | % | ASTM D638 |
| Fracture | 9.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2310 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.5 | MPa | ASTM D790 |
| -- | 84.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.18 | ASTM D3702 Modified | |
| With Self-Static | 0.070 | ASTM D3702 Modified | |
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| 23°C 3 | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 4 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 117 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 128 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN72700 | LyondellBasell Industries | LDPE | Microthene® G |
| Akulon® S223-HG6 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| DENILEN M 3031 | Vamp Tech | PP, Unspecified | DENILEN |
| GTPO™ 8260 (Wire & Cable) | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |
| Epocast 1626 C1/D2 | Huntsman Advanced Materials | Epoxy | Epocast |