Generic PP, Unspecified - Talc
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 47k78d_Generic-PP-Unspecified---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 - 1.27 | g/cm³ | ASTM D792 |
| 23°C | 1.02 - 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.50 - 20 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 3.0 - 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.00 - 8.25 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.78 - 1.6 | % | ASTM D955 |
| Transverse flow : 23°C | 1.3 - 1.8 | % | ASTM D955 |
| 23°C | 8.0E-3 - 2.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.018 - 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 60 - 105 | ASTM D785 | |
| 23°C | 60 - 88 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 70 - 78 | ASTM D2240 | |
| 23°C | 62 - 68 | ISO 868 | |
| Ball Indentation Hardness | 40.0 - 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2070 - 5170 | MPa | ASTM D638 |
| 23°C | 1420 - 4010 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 19.9 - 34.6 | MPa | ASTM D638 |
| Yield, 23°C | 16.9 - 36.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 16.0 - 32.2 | MPa | ASTM D638 |
| Fracture, 23°C | 1.95 - 32.6 | MPa | ISO 527-2 |
| 23°C | 25.3 - 33.9 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 4.9 - 10 | % | ASTM D638 |
| Yield, 23°C | 2.0 - 10 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 38 | % | ASTM D638 |
| Fracture, 23°C | 2.2 - 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1330 - 3680 | MPa | ASTM D790 |
| 23°C | 2.02 - 3260 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 32.5 - 55.0 | MPa | ASTM D790 |
| 23°C | 23.6 - 72.0 | MPa | ISO 178 |
| Yield, 23°C | 44.6 - 64.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.2 - 6.7 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 65 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 20 - 67 | J/m | ASTM D256 |
| 23°C | 1.0 - 40 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 25 - 1400 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 0.565 - 9.04 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.452 - 1.98 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 105 - 136 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 107 - 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 58.5 - 82.5 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 53.0 - 111 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.5 - 155 | °C | ASTM D1525 |
| -- | 84.0 - 162 | °C | ISO 306 |
| Melting Temperature (DSC) | 149 - 160 | °C | ISO 3146 |
| CLTE - Flow | 5.9E-5 - 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+5 - 1.0E+15 | ohms | ASTM D257 |
| -- | 1.0E+13 - 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+2 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 8.4E+15 - 1.1E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 24 - 120 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C) | 2.30 - 2.50 | ASTM D150 | |
| Comparative Tracking Index | 595 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 642 - 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.0 - 94.0 | °C | |
| Drying Time | 1.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.049 - 0.051 | % | |
| Rear Temperature | 163 - 225 | °C | |
| Middle Temperature | 184 - 230 | °C | |
| Front Temperature | 205 - 240 | °C | |
| Nozzle Temperature | 205 - 240 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 37.7 - 55.8 | °C | |
| Injection Pressure | 6.55 - 96.2 | MPa | |
| Holding Pressure | 5.17 - 7.20 | MPa | |
| Back Pressure | 0.150 - 12.5 | MPa | |
| Screw Speed | 79 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE DMDC-1210 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| EMERGE™ PC 4310-10 | Trinseo | PC | EMERGE™ |
| Hifax 5519/1 G 1750 | LyondellBasell Industries | PP Copolymer | Hifax |
| Lustran® SAN CN27 | INEOS Styrolution Group GmbH | SAN | Lustran® SAN |
| NORYL™ NH6020 resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |