PRE-ELEC® PE 1271
| Category: | LDPE+LLDPE , Low Density Polyethylene + LLDPE |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 47aPCV_PRE-ELEC-PE-1271.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PE 1271 is a carbon black filled conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. In addition to a low electrical resistivity PRE-ELEC® PE 1271 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include blown mono- or co-extrusion film for ESD bags and innerliners, bags or layflat tubing for hazardous powders. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 35 | g/10 min | |
| 190°C/5.0 kg | 1.7 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Across Flow : Yield | 15.2 | MPa | ASTM D638 |
| Flow : Yield | 21.4 | MPa | ASTM D638 |
| Across Flow : Yield | 15.0 | MPa | ISO 527-2 |
| Flow : Yield | 21.0 | MPa | ISO 527-2 |
| Across Flow | 22.1 | MPa | ASTM D638 |
| Flow | 24.1 | MPa | ASTM D638 |
| -- 1 | 22.0 | MPa | ISO 527-2 |
| 0.400 mm 2 | 24.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Across Flow : Yield | 17 | % | ASTM D638, ISO 527-2 |
| Flow : Yield | 13 | % | ASTM D638, ISO 527-2 |
| Across Flow : Break | 600 | % | ASTM D638 |
| Flow : Break | 590 | % | ASTM D638 |
| Break, 0.300 mm 3 | 600 | % | ISO 527-2 |
| Break, 0.300 mm 4 | 590 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Barrel Temperature | 160 to 200 | °C | |
| Blow-up Ratio | > 1.80 |
| Note Message | |
|---|---|
| 1 . | .4 mm thickness, Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-80UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ACCUCOMP™ HP0315L | ACLO Compounders Inc. | PP Homopolymer | ACCUCOMP™ |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| NYCOA Polyamide 2076 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| GERMAFORM 9 MF 10 | Kunststoff-Kontor-Hamburg GmbH | Acetal (POM) Copolymer | GERMAFORM |