ALCUDIA® LDPE 2221FG
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 45sCoR_ALCUDIA-LDPE-2221FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 2221FG is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for thin blown film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains slip (erucamide), antioxidant and antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 150 to 180°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.10 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 26.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 5.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 3.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 85 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC710 | Polytech & Net Gmbh | EVA | Polytech & Net |
| DynaMix™ 2035-LM | Polymer Dynamix | Nylon 66 | DynaMix™ |
| OnForce™ LFT 5200-5001 FR Natural | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |
| Hifax EKC 287P G22524 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 9812-65 Brown 7418 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |