Badamid® PA612 CF30
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 45ef7t_Badamid-PA612-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA612 CF30 is a Polyamide 612 (Nylon 612) material filled with 30% carbon fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA612 CF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.60 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16500 | 14900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 190 | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 23°C) | 2.0 | 2.6 | % | ISO 527-2/1A/5 |
| Flexural Stress (23°C, 4.00 mm) | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 70 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 212 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 218 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+2 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | < 100 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2530-NT | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| REPOL® SS35N | Reliance Industries Limited | PP Homopolymer | REPOL® |
| Surlyn® 9520 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| ENFLEX VX-412-62A | Ravago Group | PP+EPDM | ENFLEX |
| 3M™ Dyneon™ Fluoroelastomer FE 5623 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |