Generic XLPE
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 45CZVp_Generic-XLPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic XLPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.905 - 0.974 | g/cm³ | ASTM D792 |
| 23°C | 0.921 - 0.936 | g/cm³ | ISO 1183 |
| -- | 0.918 - 0.983 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.47 - 1.26 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.32 - 2.1 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.93 - 2.2 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 46 - 64 | ASTM D2240 | |
| 23°C | 52 - 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6.00 - 685 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 15.8 - 31.0 | MPa | ASTM D638 |
| Yield, 23°C | 15.0 - 22.1 | MPa | ISO 527-2 |
| Fracture, 23°C | 11.0 - 31.0 | MPa | ASTM D638 |
| 23°C | 19.9 - 20.0 | MPa | ASTM D638 |
| 23°C | 9.80 - 14.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 340 - 520 | % | ASTM D638 |
| Fracture, 23°C | 140 - 460 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 11.5 - 16.5 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 160 - 300 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -79.2 - -74.4 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 - 127 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0E+2 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 10 - 1.1E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 20 - 47 | kV/mm | ASTM D149 |
| 23°C | 22 - 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.30 - 3.70 | ASTM D150 | |
| 23°C | 2.29 - 2.31 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 3.0E-4 - 0.010 | ASTM D150 | |
| 23°C | 3.0E-4 - 5.1E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 29 - 36 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 - 60.0 | °C | |
| Drying Time | 4.0 - 5.2 | hr | |
| Cylinder Zone 1 Temp. | 128 - 175 | °C | |
| Cylinder Zone 2 Temp. | 139 - 185 | °C | |
| Cylinder Zone 3 Temp. | 144 - 192 | °C | |
| Cylinder Zone 4 Temp. | 149 - 207 | °C | |
| Cylinder Zone 5 Temp. | 173 - 221 | °C | |
| Melt Temperature | 129 - 136 | °C | |
| Die Temperature | 159 - 227 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic XLPEThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L MAT-4 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Fainplast PVC MPH 75/H | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| FR-PET® BLR6001MZ | Polyplastics Co., Ltd. | PET | FR-PET® |
| Geon™ Vinyl Dry Blend E7857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| Kepamid® 1825GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |