LNP™ STAT-LOY™ PF306 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 457GTR_LNP-STAT-LOY-PF306-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. Also known as: LNP* STAT-LOY* Compound PF-30 Product reorder name: PF306 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.82 | % | ISO 294-4 |
| Flow : 24 hr | 0.28 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 5.1 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- | 7480 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 93.8 | MPa | ASTM D638 |
| Yield | 83.0 | MPa | ISO 527-2 |
| Break | 93.8 | MPa | ASTM D638 |
| Break | 83.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.7 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2 |
| Break | 2.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 2 | 7.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 960 | J/m | ASTM D4812 |
| 23°C 3 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 17.0 | J | ASTM D3763 |
| -- | 6.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 203 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 201 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 185 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 182 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.0 to 11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HG960E | LyondellBasell Industries | PP Homopolymer | Supol |
| 4TECH® 9A22720 E-MH | 4Plas | Nylon 66 | 4TECH® |
| CYCOLAC™ MG47F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| LNP™ THERMOCOMP™ RC003 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| PENTAMID A L1 H black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |