Arnite® AV2 370 XL-T
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 445vrG_Arnite-AV2-370-XL-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Arnite® AV2 370 XL-T is a Polyethylene Terephthalate (PET) material filled with 35% glass fiber. It is available in Europe. Important attributes of Arnite® AV2 370 XL-T are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.45 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Melting Temperature 1 | 255 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 4.0E-5 | cm/cm/°C | |
| Thermal Conductivity | ASTM E1461 | ||
| -- 2 | 0.80 | W/m/K | |
| -- 3 | 1.7 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 1.1 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1.00 GHz) | 14.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 12 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | through plane |
| 3 . | in plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMV Blanc 5 P20 D | Arkema | Nylon 11 | Rilsan® |
| THERMOLAST® K TF9CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wanthane® WHT-1172 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| HI-ZEX™ 1608J | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| MACOMASS TPE MM-TPE V 3120 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |