CONTINUUM™ DGDB-2490 BK

Category:	HDPE , Bimodal Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	CONTINUUM™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	43fQ9P_CONTINUUM-DGDB-2490-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Compliance with industry standards

ASTM D 3350: step

black-PE445576C

plastic pipe research institute (PPI):TR-4

black pipe-CONTINUUM DGDB-2490 BK 100 (see note 1)

ISO PE100 pipe brand-MRS 10 @ 20°C; CRS 10 @ 20°C, 100 yr; CRS 8 @ 40°C, 90 yr; MRS 6.3 @ 60°C, 11 yr

ASTM PE4710 pipe brand-1600psi HDB @ 73 °F and 1000psi HDB @ 140 °F

National Health Foundation (NSF): Standard 14 and 61

black pipe-DGDB-2490 BK 100 (see note 1)

standard 14 and 61

Please check the regulations for complete details.

CONTINUUM™DGDB-2490 BK bimodal polyethylene resin was prepared by UNIPOL™II process technology. This product can be used in the field of pipeline construction. These pipelines are required to withstand water pressure strength for a long time, and have the ability to resist slow crack generation and rapid crack growth. Applicable applications include natural gas transmission and distribution pipelines, industrial pipelines, mining, sewage and municipal water supply and drainage pipelines.

remarks:
(1) under appropriate processing conditions, carbon black masterbatch DFNF-0092 (6.5%) can be added to extrude the primary color resin.

General Information
Agency Ratings	ASTM D 3350 PE445576C ASTM PE4710 ISO PE 100 NSF 14 NSF 61 PPI TR-4
Forms	Particle
Processing Method	Profile extrusion molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity			ASTM D792
-- ¹	0.949	g/cm³	ASTM D792
-- ²	0.959	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/2.16 kg	0.080	g/10 min	ASTM D1238
190°C/21.6 kg	7.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ³(Yield)	24.8	MPa	ASTM D638
Tensile Elongation ⁴(Break)	740	%	ASTM D638
Flexural Modulus	1030	MPa	ASTM D790B
Resistance to rapid crack propagation, Pc ⁵	> 12.0	bar	ISO 13477
Resistance to rapid crack propagation, Tc ⁶		°C	ISO 13477
Slow crack propagation PENT ⁷	> 10000	hr	ASTM F1473
Hydrostatic strength ⁸			ASTM D1598
1798 psi (12.4 MPa) : 20°C	> 100	hr	ASTM D1598
798 psi (5.5 MPa) : 80°C	> 1000	hr	ASTM D1598

Thermal	Nominal Value	Unit	Test Method
Thermal Stability	> 220	°C	ASTM D3350

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact ⁹(23°C)	490	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature ¹⁰	< -75.0	°C	ASTM D746A

Extrusion	Nominal Value	Unit
Melt Temperature	193 - 227	°C

Extrusion instructions
制造条件：螺杆类型：高质量 HDPE（对于完全熔解最好使用阻隔）熔体温度范围：380-440°F (193-225°C)

Note Message
1 .	Natural resin
2 .	The natural resin was extruded under normal conditions using a carbon black masterbatch DFNF-0092 (6.5%).
3 .	Prepare compression molded fittings according to ASTM D 14703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time.
4 .	Prepare compression molded fittings according to ASTM D 14703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time.
5 .	The natural resin was extruded under normal conditions using a carbon black masterbatch DFNF-0092 (6.5%). The pipe diameter is 10 inches IPS (25.4cm) and the standard diameter ratio (SDR) is 11.
6 .	The natural resin was extruded under normal conditions using a carbon black masterbatch DFNF-0092 (6.5%). The pipe diameter is 10 inches IPS (25.4cm) and the standard diameter ratio (SDR) is 11.
7 .	Prepare compression molded fittings according to ASTM D 14703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time.
8 .	The natural resin was extruded under normal conditions using a carbon black masterbatch DFNF-0092 (6.5%).
9 .	Prepare compression molded fittings according to ASTM D 14703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time.
10 .	Prepare compression molded fittings according to ASTM D 14703 procedure C, unless otherwise specified in the test method. Attributes will vary with molding conditions and aging time.

Resin Grade	Manufacturer	Category	Trademark
Ravago Compounds HM-230	Ravago Manufacturing Americas, LLC	LLDPE	Ravago Compounds
Karina IVORY PVC COMPOUND 810D35/ 1-C-AC-AS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
OTECH PVC OM7040-Molding	OTECH Corporation	PVC, Unspecified	OTECH PVC
Elastoflex® Bio 28110 R/T	BASF Corporation	PUR-MDI	Elastoflex®
LGG 1043	LG Polymers India Pvt. Ltd.	PS (GPPS)	LGG