Makropol® PC B3 HF UV CRLA010 PC306
| Category: | PC , Polycarbonate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Makropol® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 43GL2Y_Makropol-PC-B3-HF-UV-CRLA010-PC306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate crystal for injection molding with excellent thermal and mechanical properties, with UV protection. |
| General Information | |
|---|---|
| Additive |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Flexural Strength | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 880 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 134 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 65.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP374R | LyondellBasell Industries | PP Random Copolymer | Purell |
| SILVER® SA-2311 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| Argothane® ST-3850FS-85 | Argotec LLC | TPU, Unspecified | Argothane® |
| Lupox® GP1006FD | LG Chem Ltd. | PBT | Lupox® |
| TECHNYL STAR® S 218 V35 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |