LNP™ LUBRICOMP™ RN001S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 42cVK0_LNP-LUBRICOMP-RN001S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound NYKON R- HS Product reorder name: RN001S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 1.0 | % | |
| Flow : 24 hr | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 3910 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 84.1 | MPa | ASTM D638 |
| Yield | 69.0 | MPa | ISO 527-2 |
| Break | 84.1 | MPa | ASTM D638 |
| Break | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 3.8 | % | ASTM D638 |
| Break | 42 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 3400 | MPa | ISO 178 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.75 | ||
| vs. Itself - Static | 0.55 | ||
| Wear Factor - Washer | 103 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 2.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 2.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 231 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 76.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 301 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P4-10TC-0520 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Nylfor® B1 GF/30 H1 N NERO | SO.F.TER. SPA | Nylon 6 | Nylfor® |
| AMTOPP VA18 | Inteplast Group | PP, Unspecified | AMTOPP |
| ECOMID ARX H D05 | Nilit Plastics | Nylon 66 | ECOMID |
| Sylvin 2920-93 Green 3170 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |