LEXAN™ ML3260 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 41shPI_LEXANML3260resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN™ML3260 resin is a polycarbonate (PC) material,. This product is available in the Asia-Pacific region,. LEXAN™The main characteristics of ML3260 resin are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.50 | % | Internal method |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 83.4 | MPa | Internal method |
| Tensile Elongation (Break) | 10 | % | Internal method |
| Flexural Modulus | 4510 | MPa | ASTM D790 |
| Flexural Strength | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 58 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 139 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARVYLAN® S 5002 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Unspecified | MARVYLAN® S |
| Novalloy-S S6500L | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| FORMULA P COMP 3220 M1 | Putsch Kunststoffe GmbH | PP Copolymer | FORMULA P |
| ELASTOSIL® LR 3004/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Hostaform® LX90GC15 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |