Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | MACOMASS Verkaufs AG |
Trademark: | MACOMASS PP |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 41eEAg_MACOMASSPPMMPPHG23.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
PP homo Compound, 20% glass fibre reinforced, chemically coupled |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Appearance |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.02 - 1.06 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 - 12 | g/10 min | ISO 1133 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Ball Indentation Hardness (H 358/30) | 99.0 | MPa | ISO 2039-1 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress | > 80.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | > 3.0 | % | ISO 527-2 |
Flexural Modulus | > 3300 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | > 8.0 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (23°C) | > 28 | kJ/m² | ISO 179 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature | |||
0.45 MPa, not annealed | 158 | °C | ISO 75-2/B |
1.8 MPa, not annealed | 143 | °C | ISO 75-2/A |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Badaflex® TPE-S 70A 1000LD | Bada AG | TPE | Badaflex® |
ALCOM® PA6 900/8 GF10 MR20 SV1285-04MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
ColorRx® PE2-1000RX | LTL Color Compounders, Inc. | PE Copolymer | ColorRx® |
Hostaform® C 9021 TF XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
Leona™ 1402SH | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |