Omnix® FC-9050 Datasheet,HPPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Omnix® FC-9050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture absorption. Omnix® FC-9050 is characterized by high stiffness and strength, very good impact properties, good dimensional stability and high flow properties. This material is an economical alternative for food service applications using die-cast alloys. Omnix® FC-9050 is approved for food contact and meets FDA regulations for Omnix® FC-9050 NT 000 (natural) and Omnix® FC-9050 BK 000 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c). It processes readily using conventional injection molding machines and methods. Water-cooled molds are suitable for use with this grade. Black: Omnix® FC-9050 BK 000 Natural: Omnix® FC-9050 NT 000

General Information
Filler / Reinforcement	Glass fiber reinforced material, 50% filler by weight
Features	Good dimensional stability Rigidity, high High strength Impact resistance, good Sprayable Fast molding cycle High liquidity Hot water formability Excellent appearance
Uses	Electrical appliances Food service sector
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding Injection molding
Part Marking Code (ISO 11469)	>PAMXD6/66-GF50

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.60	g/cm³	ASTM D792
Molding Shrinkage ¹			Internal method
Vertical flow direction	0.50	%	Internal method
Flow direction	0.20	%	Internal method
Water Absorption (23°C, 24 hr)	0.27	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2
Tensile Stress (Yield)	235	MPa	ISO 527-2
Tensile Strain (Break)	2.1	%	ISO 527-2
Flexural Modulus	1500	MPa	ISO 178
Flexural Stress	340	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	13	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength	75	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	248	°C	ISO 75-2/A
Melting Temperature	260	°C	ASTM D3418

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Additional Information
Typical values shown tested on Dry as Molded samples.Standard Packaging and Labeling: Omnix® FC-9050 resin is packaged in foil lined, multiwall paper bags containing 25 kg (55 pounds) of material. Individual packages will be plainly marked with the product number, the color, the lot number, and the net weight.

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0 - 12	hr
Rear Temperature	250	°C
Front Temperature	285	°C
Processing (Melt) Temp	275 - 290	°C
Mold Temperature	80.0 - 120	°C

Injection instructions
Drying: Omnix® FC-9050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® FC-9050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

Injection instructions

Drying: Omnix® FC-9050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® FC-9050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

Note Message
1 .	Solvay test method. The shrinkage rate will change according to the design and processing conditions of components. Please contact Solvay's technical representative for more information.

Category:	HPPA , High Performance Polyamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Omnix®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	41BCGT_Omnix-FC-9050.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Propilven J-440	Propilven, S.A.	PP Impact Copolymer	Propilven
RTP EMI 262A	RTP Company	Nylon 6	RTP
Silopren® LSR 4670	Momentive Performance Materials Inc.	Silicone Rubber, LSR	Silopren®
NuSil CV1-2646	NuSil Technology	Silicone	NuSil
Bergamid™ B70 G30 H white VN8080CF UV	PolyOne Corporation	Nylon 6	Bergamid™