LNP™ LUBRICOMP™ PFL38S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40waru_LNPLUBRICOMPPFL38Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* PFL38S is a compound based on PA 6 resin, containing Glass fiber, PTFE. Added features include: Internally Lubricated, Heat Stabilized Also known as: LNP* LUBRICOMP* Compound PFL-4038 HS Product reorder name: PFL38S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 172 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11600 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 251 | MPa | ISO 178 |
| -- 4 | 244 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.63 | ASTM D3702 Modified | |
| Flexural Strain at Break 5 | 3.6 | % | ISO 178 |
| Wear Factor - Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | 216 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 203 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ GLP100 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| UBE Nylon 7034 T | UBE Engineering Plastics, S.A. | Nylon 612 | UBE Nylon |
| Unichem 6034 | Colorite Polymers | PVC, Unspecified | Unichem |
| Haysite SMC 54500 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| LNP™ THERMOTUF™ QX01581H compound | SABIC Innovative Plastics Asia Pacific | Nylon 610 | LNP™ THERMOTUF™ |