Infino HM-3301GL
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40LLgU_Infino-HM-3301GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/GF material that is used for electric and electronic parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 | g/cm³ | ASTM D792 |
| -- | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/10.0 kg | 7.0 | g/10 min | ASTM D1238 |
| 250°C/10.0 kg | 5.4 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 93 | ASTM D785 | |
| R-Scale | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 130 | MPa | ASTM D638 |
| Yield | 115 | MPa | ISO 527-2/50 |
| Break | 115 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 7700 | MPa | ASTM D790 |
| -- 3 | 7900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 200 | MPa | ASTM D790 |
| -- 5 | 153 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 146 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 143 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/B50 |
| -- | 152 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (10 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (10 MHz) | 9.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 V-1 | ||
| 3.00 mm | V-0 | ||
| 6.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 68.6 to 226 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V30 NATURAL FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Karina FUM\u00C9 MBATCH (SP31452) -E 27/ 8-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTM® 317-1B | Cytec Industries Inc. | Epoxy | LTM® |
| POLYCOMPO PE ACE30N | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |
| PENTAMID B GV10 MC20 H2 RC black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |