RTP 1303
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40Gzga_RTP-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - UL94 V-0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9650 | MPa | ASTM D638 |
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 307 to 329 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V929_02 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sanren Y3700C (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| ALCOM® PA66 910/1 GF15 MR25 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Chemlon® AT10 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| HiFill® TPU GF20 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |