AZDEL™ C220B02N
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3yYpY7_AZDEL-C220B02N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Azdel® C200B02N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural, thin walled applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.35 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179/2fnU |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| 4.00, energy to power peak | 12.0 | J | ISO 6603-2 |
| 4.00, total impact penetration energy | 28.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (4.00 mm) | 4000 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 166 | °C | ISO 3146 |
| Additional Information |
|---|
| Mass Per Unit Area, Azdel Test Method: 4.050 kg/m²Thickness, Azdel Test Method: 3.9 mmDensity, ISO 1183 Test Method: 1.04 g/cm³Density, ISO 1183 Test Method, Molded Plaque: 1.07 g/cm³Recrystallizing Temperature, ISO 3146 Test Method: 115 °CCTLE, Azdel Test Method, -30°C to 0°C, 3mm: 5.2e-5 1/°CCTLE, Azdel Test Method, 0°C to 120°C, 3mm: 3.8e-5 1/°CBlank Heat Parameters-Internal Temperature: 190 to 215°C-Surface Temperature: 205 to 220°C-Typical Heating Time for IR-System: 180 to 240°C-Typical Heating Time for Hot Air System: 240 to 480°CMould Temperature: 30 to 90°CMoulding Preasure: 150 to 250 barMinimum Pressing Speed: 20 mm/secTotal Cycle Time: 30 to 90 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT PCR ABS M35-300PCR | NEXT Specialty Resins, Inc. | ABS | NEXT PCR |
| AKROMID® A3 GM 20/10 S1 natural (1217) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Chiao Fu PA66/6 MB312G33 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| EPIMIX POM GFR 25 NC | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| Hanwha Total PP HY110 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |