Amodel® A-1130 FW Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applications. Black: A-1130 FW BK 324

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	PTFE lubricant
Features	Good dimensional stability Low friction coefficient Rigid, good High strength Good creep resistance Good chemical resistance Good wear resistance
Uses	Bushing Gear Filter Bearing
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.55	g/cm³	ISO 1183/A

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11200	MPa	ISO 527-2
Tensile Stress (Break)	187	MPa	ISO 527-2
Tensile Strain (Break)	2.0	%	ISO 527-2
Flexural Modulus	9580	MPa	ISO 178
Flexural Stress	252	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	285	°C	ISO 75-2/A
Melting Temperature	313	°C	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	110	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	329 - 343	°C
Mold Temperature	135	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Resin Grade	Manufacturer	Category	Trademark
GAPEX® RPP15EU58HB	Ferro Corporation	PP, Unspecified	GAPEX®
HIPOLEN P® MA 21	HIPOL A.D.	PP Homopolymer	HIPOLEN P®
Petrothene® NA480145	LyondellBasell Industries	LDPE	Petrothene®
Pro-fax SL994MW	INDELPRO, S.A. de C.V.	PP Random Copolymer	Pro-fax
Hostacom TRC 160N C12380	LyondellBasell Industries	PP Copolymer	Hostacom

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3yVYgG_Amodel-A-1130-FW.pdf
PRICE:	Order Products email sales@su-jiao.com