LNP™ STAT-KON™ 115EM4A compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3xXtWT_LNP-STAT-KON-115EM4A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* 115EM4A is an electrically conductive compound based on PPE+PS containing carbon powder. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 69.0 | MPa | Internal Method |
| Tensile Elongation (Break) | 6.0 | % | Internal Method |
| Flexural Modulus | 3340 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 163 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1922 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Alpha PVC GW 3035-VW1 NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| BLUESTAR® POM BS090A | Beijing Ranger Chemical Co., Ltd. | Acetal (POM) Copolymer | BLUESTAR® POM |
| Durethan® B 31 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| PLUSTEK PA830 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |