LNP™ STAT-KON™ DE0021E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3xSRrg_LNP-STAT-KON-DE0021E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1002 EM FR ECO Product reorder name: DE0021E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.29 to 0.43 | % | ISO 294-4 |
| Flow : 24 hr | 0.060 to 0.32 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9160 | MPa | ASTM D638 |
| -- | 9360 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 115 | MPa | ASTM D638 |
| Break | 112 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.8 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8220 | MPa | ASTM D790 |
| -- | 8500 | MPa | ISO 178 |
| Flexural Strength | 170 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 7.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.40 | J | ASTM D3763 |
| -- | 7.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 93.3 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 96.6 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 254 to 288 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 80S7351 | The Matrixx Group, Inc. | PET | Matrixx |
| SEMICOSIL® 970 TC A/B | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Texalan® 5 Series 585A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| AMTOPP TE18 | Inteplast Group | PP, Unspecified | AMTOPP |
| Karina BLACK PVC COMPOUND TR-751D48/ 1-E-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |