LNP™ STAT-KON™ DD0009P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3w7Rqb_LNPSTATKONDD0009Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound D-EP V-1 Product reorder name: DD0009P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.78 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2620 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 64.1 | MPa | ASTM D638 |
| Yield | 59.9 | MPa | ISO 527-2 |
| Fracture | 54.7 | MPa | ASTM D638 |
| Fracture | 53.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.8 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2 |
| Fracture | 10 | % | ASTM D638 |
| Fracture | 9.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2830 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | 103 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 9.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2100 | J/m | ASTM D4812 |
| 23°C 3 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.5 | J | ASTM D3763 |
| -- | 35.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 128 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 266 - 288 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1009FM | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Sylvin 8325-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Bakelite® PF 7595 | Hexion Inc. | Phenolic | Bakelite® |
| ExxonMobil™ PPU0009F | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Starex LX-9140 | LOTTE ADVANCED MATERIALS CO., LTD. | ASA | Starex |