EPO-TEK® E2101
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ueidy_EPO-TEK-E2101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® E2101 is a two component, thixotropic, electrically conductive adhesive. It may be used for circuit assembly and semiconductor applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 27 | ppm | |
| K+ | 1 | ppm | |
| Na+ | 10 | ppm | |
| NH4+ | 80 | ppm | |
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 401 | °C | TGA |
| Die Shear Strength - >5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 7.26 | GPa | |
| Thixotropic Index | 3.90 | ||
| Weight Loss on Heating | |||
| 200°C | 0.37 | % | |
| 250°C | 0.61 | % | |
| 300°C | 0.90 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 90.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.8E-5 | cm/cm/°C | |
| -- 3 | 1.9E-4 | cm/cm/°C | |
| Thermal Conductivity | 2.5 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 3.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Silver | ||
| -- 5 | Silver | ||
| Density | |||
| Part A | 2.34 | g/cm³ | |
| Part B | 4.57 | g/cm³ | |
| Viscosity 6(23°C) | 15 to 18 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 7200 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 68 | ||
| Lap Shear Strength (23°C) | 6.56 | MPa | |
| Volume Resistivity (23°C) | < 5.0E-4 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P30N07 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Unichem 7305 | Colorite Polymers | PVC, Unspecified | Unichem |
| Electrafil® PS-31/EC | Techmer Engineered Solutions | PS (GPPS) | Electrafil® |
| ELASTOSIL® R 401/30 S | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| PLUSTEK RA502 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |