Sasol Polymers PP HNR101

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3u9cI0_Sasol-Polymers-PP-HNR101.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

High flow

Suitable for short spin and long spin staple fibre applications

Offers easy extrusion processability when used for producing:

Medium to high denier staple fibre

Continuous multifilament (CF) on multi position spin / draw / wind or short spin / warp draw / wind processes

Applications
Extrusion

Needle punched carpets

Filtration cloth

Sewing yarns

Narrow weave strapping

General Information
Additive	Anti-gas fading
Features	Food Contact Acceptable Gas-fading Resistant Good Processability High Flow Homopolymer
Uses	Filtration Media Staple Fibers Strapping Yarn
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	12	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	70.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1550	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	34.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	8.5	%
Break	> 50	%
Flexural Modulus	1500	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.8	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	85.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	53.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	154	°C	ISO 306/A120
--	90.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Extrusion	Nominal Value	Unit
Hopper Temperature	40.0 to 60.0	°C
Cylinder Zone 1 Temp.	200 to 280	°C
Cylinder Zone 2 Temp.	240 to 280	°C
Cylinder Zone 3 Temp.	240 to 280	°C
Cylinder Zone 4 Temp.	240 to 280	°C
Cylinder Zone 5 Temp.	220 to 280	°C
Melt Temperature	220 to 280	°C
Die Temperature	220 to 240	°C

Resin Grade	Manufacturer	Category	Trademark
Vi-Chem PVC VNC90-80E	Vi-Chem Corporation	PVC, Unspecified	Vi-Chem PVC
Wellamid® GF1398-BK1	Wellman Engineering Resins	Nylon 66	Wellamid®
AIE PPO 9010F-S140A	Asia International Enterprise (Hong Kong) Limited	PPE+PS	AIE PPO
Estane® 58887 TPU	Lubrizol Advanced Materials, Inc.	TPU-Polyether	Estane®
EPO-TEK® T7110	Epoxy Technology Inc.	Epoxy	EPO-TEK®