LNP™ THERMOTUF™ WF003I compound
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3tt6WW_LNP-THERMOTUF-WF003I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* WF003I is a compound based on PBT resin containing 15% Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound WF-1003 HI Product reorder name: WF003I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.95 | % | ISO 294-4 |
| Flow : 24 hr | 0.75 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5010 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 78.0 | MPa | ISO 527-2 |
| Break | 79.8 | MPa | ASTM D638 |
| Break | 76.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | |||
| -- | 4590 | MPa | ASTM D790 |
| -- | 4710 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 135 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 1 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 2 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.2 | J | ASTM D3763 |
| -- | 4.22 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 201 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® R123 TR25 | Razin™ Engineering Plastics | PP+EPDM | Razalen® |
| SMOKEGUARD™ III 1056 NATURAL | AlphaGary | PVC, Semi-Rigid | SMOKEGUARD™ III |
| HiFill FR® PA6/6 FR IM | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| Luxus PP 16192 | Luxus Limited | PP, Unspecified | Luxus PP |
| Sylvin 5132-75 Clear Red 6191 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |