Hifax 7430 XEP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3tIMHg_Hifax-7430-XEP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax 7430 XEP is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell' s proprietary Catalloy process technology. It is a high melt flow, medium-high flexural modulus, highly crystalline copolymer with good balance of impact and stiffness. It is primarily used in interior trim applications requiring low temperature high speed impact performance. It is also used as a component in compounded materials for automotive and industrial applications. The grade is available in natural pellet form. For regulatory compliance information see Hifax 7430 XEP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 56 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 20.0 | MPa | |
| Break, 23°C | 14.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 32 | % | |
| Flexural Modulus - Chord 1(23°C) | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C, Complete Break | 5.3 | kJ/m² | |
| 23°C, Complete Break | 11 | kJ/m² | |
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -40°C, 3.20 mm, Total Energy, Ductile Failure | 28.0 | J | |
| 23°C, 3.20 mm, Peak Energy, Ductile Failure | 18.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 131 | °C | ISO 306/A50 |
| Melting Temperature | 161 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 2102GBM | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Andur 6500 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| ExxonMobil™ HDPE HPA 020 Wire & Cable | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| HiFill® PA6 0325 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| ESTOPLAST XU 6100BB02 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |