TechnoMid PA6 S GF 15 SZ

Category:	Nylon 6 , Polyamide 6
Manufacturer:	TechnoCompound GmbH
Trademark:	TechnoMid
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3sgCdu_TechnoMidPA6SGF15SZ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High mechanical strength and stiffness

High thermal stability

High toughness at low temperatures

Excellent sliding friction behavior

Optimal flow characteristics for challenging applications

Suitable for low-warpage injection molding parts

Also "cross-linkable" available

Typical Applications

Automotive: Radiator grills, exterior door handles, door sills, door-mirror housings, wheel covers, steering wheels, fastening clips, gearshift-lever housings, shift links, headlamp housings, power and fuse boxes, front-End-Modules, bumper stiffener, air intake modules, engine covers "Beauty-Cover", valve bonnet and cylinder head covers, chain guides, toothed belt covers, ventilation and cooling systems...

Household: Chair frames, furniture casters, craft toll shafts...

Sanitation: Handles, fittings, fixtures and fans

Plumbing: Wall dowels , fasteners, clamps for cables and pipes

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Features	Low warpage Low Temperature Flexibility Rigidity, high High strength Good liquidity Thermal stability, good
Uses	Handle Pipe components Household goods Fasteners Accessories Application in Automobile Field Shell Bathroom products
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Molding Shrinkage ¹			ISO 294-4
Transverse flow	0.70	%	ISO 294-4
Flow	0.20	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C	7.5	%	ISO 62
Equilibrium, 23°C, 50% RH	2.4	%	ISO 62
Viscosity Number	150	cm³/g	ISO 307

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness ²	145	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5500	MPa	ISO 527-2/1
Tensile Stress
Yield	110	MPa	ISO 527-2/50
Fracture	110	MPa	ISO 527-2/5
Tensile Strain
Yield	4.0	%	ISO 527-2/50
Fracture	4.0	%	ISO 527-2/5
Flexural Modulus ³	4500	MPa	ISO 178
Flexural Stress ⁴	150	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	6.0	kJ/m²	ISO 179/1eA
23°C	13	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	60	kJ/m²	ISO 179/1eU
23°C	65	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	210	°C	ISO 75-2/B
1.8 MPa, not annealed	200	°C	ISO 75-2/A
8.0 MPa, not annealed	60.0	°C	ISO 75-2/C
Vicat Softening Temperature	200	°C	ISO 306/B120
Melting Temperature ⁵	220	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 80°C	3.0E-5 - 5.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 80°C	9.0E-5 - 1.1E-4	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Dielectric Strength (1.00 mm)	35	kV/mm	IEC 60243-1
Relative Permittivity (1 MHz)	3.70		IEC 60250
Comparative Tracking Index (Solution A)	550	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.8 mm)	HB		UL 94

Note Message
1 .	260°C / WZ 80°C, 600 bar
2 .	358 N
3 .	2.0 mm/min
4 .	2.0 mm/min
5 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
RONFALIN® TXE95	A. Schulman Europe	ABS	RONFALIN®
SUPREME Specialty PS SP243	Supreme Petrochem Ltd.	PS (Specialty)	SUPREME Specialty PS
Latene® AG7H2 G/50	LATI S.p.A.	PP Homopolymer	Latene®
Keliren® CM3685	Hangzhou Keli Chemical Co., Ltd.	CPE	Keliren®
PARAPET GR00100	Kuraray Co., Ltd.	Acrylic (PMMA)	PARAPET