Ultramid® B3WGM24 sw23228
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3sSuYk_Ultramid-B3WGM24-sw23228.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass-fibre and mineral reinforced heat stabilised injection moulding grade for industrial parts having medium to highrigidity and high dimensional stability, used e.g. for automobile engine covers, housings and automotive door handles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.61 | -- | % | ISO 294-4 |
| Flow direction | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.9 - 7.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 - 2.5 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9300 | 4200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 10 | % | ISO 527-2 |
| Flexural Modulus | 8400 | -- | MPa | ISO 178 |
| Flexural Stress | 180 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 52 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/A | |||
| -30°C | 4.5 | 4.5 | kJ/m² | ISO 180/A |
| 23°C | 6.0 | 13 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 3.4E-5 - 3.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 6.0E-5 - 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1300 | -- | J/kg/°C | |
| Maximum operating temperature- short cycle operation | 180 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+10 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 134518 | RTP Company | PP, Unspecified | RTP |
| PrimaFlex® CP 0212 | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Aurora PVC AP1250 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| JSR EPR EP24 | JSR Corporation | EPDM | JSR EPR |
| LubriOne™ NL-30CF/15T Black | PolyOne Corporation | Nylon 612 | LubriOne™ |