POLYFLAM® RPP 3225 GW
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3sFxhX_POLYFLAMRPP3225GW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% glass fibre reinforced flame-retardant PP-Homopolymer; without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7650 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 69.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.6 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.2 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.5 mm | 960 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.5 mm | 850 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SORVEX 1200 | Sorensen Ventures | PBT | SORVEX |
| Spartech PE Ultros SRP™ Co-Extruded Skid-Resistant | Spartech Plastics | PE Alloy | Spartech |
| NITRIFLEX NP-6121 | NITRIFLEX | NBR | NITRIFLEX |
| Elastollan® B 60 A ESD M | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Daelim Po1y® XP5300 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |