NEFTEKHIM PE 5120N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3rxLdd_NEFTEKHIM-PE-5120N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts. Stabilization recipe: antacid, antioxidant, thermostabilizer, sliding agent, antiblocking agent, processing agent, dispersing agent. Application: high strength tubular film, improved film processability and surface quality. Technical requirements: TU 2211-145-05766801-2008 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 to 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 to 1.3 | g/10 min | ASTM D1238 |
| Gel Content 1 | |||
| > 200.0 µm | 250 | pcs/m² | |
| 200.0 to 500.0 µm | 245 | pcs/m² | |
| 500.0 to 1000.0 µm | 5.00 | pcs/m² | |
| > 1.00 mm | 0.00 | pcs/m² | |
| Melt Flow Ratio - MFR 21.6 kg/MFR 2.16 kg | < 30.0 | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD | 130 | MPa | |
| 2% Secant, TD | 140 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 50.0 | MPa | |
| TD : Yield | 35.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 700 | % | |
| TD : Break | 950 | % | |
| Dart Drop Impact | 210 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 240 | g | |
| TD | 480 | g |
| Note Message | |
|---|---|
| 1 . | p.6 Attachment A TU 2211-14505766801 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 82109 | RTP Company | PEI | RTP |
| Ranger PBT PBT-403-M-G30 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TUFNYL® RXXIN NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Hifax CB 1128 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LNP™ THERMOCOMP™ RF008 compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |