Petra® 130 BK-112
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3rW7tY_Petra-130-BK-112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 130 BK-112 is a 30% glass fiber reinforced, black pigmented polyethylene terephthalate injection molding compound. It exhibits a superb combination of performance properties including good strength and stiffness at elevated temperatures. It also has good chemical resistance and dimensional stability, and adequate ductility for most applications. Applications Petra 130 BK-112 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 145 | MPa | ASTM D638, ISO 527-2 |
| Break, -40°C | 211 | MPa | ISO 527-2 |
| Break, 121°C | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8760 | MPa | ASTM D790 |
| 23°C | 8250 | MPa | ISO 178 |
| Flexural Strength (23°C) | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.5 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 95 | J/m | ASTM D256 |
| -40°C | 8.5 | kJ/m² | ISO 180 |
| 23°C | 9.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 235 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Peak Melting Temperature | 245 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 140 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 GV 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Adell PP ER-34 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Braskem PP FP450WV | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Anjacom® R050/85S Black 91010 | Almaak International GmbH | PC+ABS | Anjacom® |
| Sylvin 4215-72 White 1217-1 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |