TOTAL Polypropylene PPH 11012
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3qaqLF_TOTAL-Polypropylene-PPH-11012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 11012 is a nucleated controlled-rheology antistatic homopolymer with a high Melt Flow Index of 55 g/10 min. Polypropylene PPH 11012 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots & tubs, salad trays, caps & closures and video cassette boxes. Polypropylene PPH 11012 has a highly antistatic nature that allows for shorter cycle times and easy demoulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 115084 C | RTP Company | PC | RTP |
| NYLAFORCE® dynamic A 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | NYLAFORCE® dynamic |
| Evoprene™ G 992 | AlphaGary | SEBS | Evoprene™ G |
| Kingfa PBT RG15 | Kingfa | PBT | Kingfa PBT |
| MAJORIS DBF334E/8-8229 | AD majoris | HDPE | MAJORIS |