NORYL™ PX5558 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3qUGFv_NORYL-PX5558-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass reinforced, high flow PPO. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.20 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7760 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 108 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 100 mm Span 4 | 7170 | MPa | |
| 50.0 mm Span 5 | 8340 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Break, 50.0 mm Span 6 | 162 | MPa | |
| Break, 100 mm Span 7 | 131 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 260 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 14.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 8 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 to 104 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 238 to 288 | °C | |
| Middle Temperature | 249 to 293 | °C | |
| Front Temperature | 260 to 299 | °C | |
| Nozzle Temperature | 271 to 299 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-15G | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Lumiflon® LF-710F | Asahi Glass Co., Ltd. | Fluoropolymer | Lumiflon® |
| Petrothene® GA502023 | LyondellBasell Industries | LLDPE | Petrothene® |
| POLYCOMPO PP J106G | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| Marlex® D170DK | Chevron Phillips Chemical Company LLC | mLLDPE | Marlex® |