LNP™ THERMOTUF™ VX99810 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3prPC4_LNP-THERMOTUF-VX99810-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF VX99810 is a compound based on Super Tough Nylon resin containing Proprietary Filler(s). Added feature of this material is: High Impact. Also known as: LNP* THERMOTUF* Compound PDX-V-99810 Product reorder name: VX99810 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 1.2 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4660 | MPa | ASTM D638 |
| -- | 4420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 74.4 | MPa | ASTM D638 |
| Yield | 73.0 | MPa | ISO 527-2/5 |
| Break 3 | 69.7 | MPa | ASTM D638 |
| Break | 70.5 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/5 |
| Break 5 | 4.5 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3090 | MPa | ASTM D790 |
| -- 7 | 3240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 710 | J/m | ASTM D4812 |
| 23°C 9 | 46 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 7.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 238 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 230 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 184 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylite® ProCast PLUS 32144-38 | Reichhold Chemicals, Inc. | Polyester, TS | Polylite® ProCast PLUS |
| UNITIKA Nylon 6 A1030FR | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| HI-ZEX™ 7800M | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| TECACOMP® PA66 TC black 3989 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Sylvin 9790-60 Green 3216 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |