VALOX™ 4022 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3plOBv_VALOX-4022-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 4022 is a 20% high strength glass fibre reinforced PBT injection moulding resin, with improved mechanical properties. Applications : Spotlights, appliance housings and handles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 40 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 16.0 | cm³/10min | |
| 250°C/5.0 kg | 23.0 | cm³/10min | |
| 265°C/5.0 kg | 30.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.30 to 0.70 | % | |
| Across Flow | 0.40 to 1.0 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 130 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 7400 | MPa | ASTM D638 |
| -- | 7300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 120 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/5 |
| Break 4 | 120 | MPa | ASTM D638 |
| Break | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 6 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 5900 | MPa | ASTM D790 |
| -- 8 | 6200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 180 | MPa | ISO 178 |
| -- | 175 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 170 | MPa | ASTM D790 |
| Break, 50.0 mm Span 10 | 170 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 20 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 12 | 5.0 | kJ/m² | ISO 179/1eA |
| -30°C | 9.0 | kJ/m² | ISO 179/2C |
| 23°C 13 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 14 | 30 | kJ/m² | ISO 179/1eU |
| -30°C | 42 | kJ/m² | ISO 179/2U |
| 23°C 15 | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 42 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 75 | J/m | ASTM D256 |
| 0°C | 75 | J/m | ASTM D256 |
| 23°C | 75 | J/m | ASTM D256 |
| -30°C 16 | 8.0 | kJ/m² | ISO 180/1A |
| 0°C 17 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 18 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 560 | J/m | ASTM D4812 |
| 23°C | 560 | J/m | ASTM D4812 |
| -30°C 19 | 35 | kJ/m² | ISO 180/1U |
| 23°C 20 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 21 | 220 | °C | ISO 75-2/Be |
| 0.45 MPa, Unannealed, 64.0 mm Span 22 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 23 | 205 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 24 | 200 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525, ISO 306/A50 14 25 |
| -- | 215 | °C | ASTM D1525, ISO 306/B50 15 26 |
| -- | 210 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 1.8E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | ASTM D149, IEC 60243-1 | ||
| 0.800 mm, in Oil | 26 | kV/mm | |
| 1.60 mm, in Oil | 24 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Dielectric Constant | |||
| 1 MHz | 3.60 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.20 | IEC 60250 | |
| 60 Hz | 3.20 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.015 | ASTM D150, IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.840 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 750 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 140 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 120*10*4 mm |
| 22 . | 80*10*4 mm |
| 23 . | 120*10*4 mm |
| 24 . | 80*10*4 mm |
| 25 . | Rate A (50°C/h), Loading 2 (50 N) |
| 26 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGN4029 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| CALP MRP430 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| DuraFlex 606 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| LG PVC LS080S | LG Chem Ltd. | PVC, Unspecified | LG PVC |
| LG PS 50IS | LG Chem Ltd. | PS (HIPS) | LG PS |