RTP 400 TFE 20
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3pbf5f_RTP-400-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 96.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, 0.25in: 6 mil/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® E115i | Celanese Corporation | LCP | VECTRA® |
| Cevian®-N 020, 020SF | Daicel Polymer Ltd. | SAN | Cevian®-N |
| ELASTOSIL® R 401/10 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Petrothene® GA502119 | LyondellBasell Industries | LLDPE | Petrothene® |
| LNP™ LUBRICOMP™ RX06480 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |