LNP™ STAT-KON™ ZE0039 compound
| Category: | Polyphenylene, Unspecified , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3pFld5_LNPSTATKONZE0039compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber. Also known as: LNP* STAT-KON* Compound ZC-1003 FR Product reorder name: ZE0039 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.30 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.086 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11700 | MPa | ASTM D638 |
| -- | 11000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 112 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2 |
| Fracture | 112 | MPa | ASTM D638 |
| Fracture | 105 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.2 | % | ASTM D638 |
| Yield | 1.1 | % | ISO 527-2 |
| Fracture | 1.2 | % | ASTM D638 |
| Fracture | 1.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8960 | MPa | ASTM D790 |
| -- | 10600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 117 | MPa | ASTM D790 |
| -- | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 3 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 11.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 112 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 113 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 104 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 106 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 2.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 - 288 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 299 - 310 | °C | |
| Processing (Melt) Temp | 299 - 304 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 GF30 FRV0 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Vyncolit® 51-01 CAFR | Vyncolit N.V. | DAP | Vyncolit® |
| Hostacom TKC451N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LNP™ STAT-KON™ PFD04S compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| PLUSTEK PA313G43 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |