Delrin® 500AL NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3p9mLZ_Delrin-500AL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.7 | % | |
| Flow | 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 23 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2400 | MPa | |
| 1000 hr | 1600 | MPa | |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 130 | kJ/m² | |
| 23°C | 160 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 164 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.2E-4 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Raditer® B RVA100 | Radici Plastics | PBT | Raditer® |
| Sinvicomp SFW10500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TECAPEI™ GF30 | Ensinger Inc. | PEI | TECAPEI™ |
| Nanjing Hongrui PA66 A3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| ULTEM™ HU1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |