Maxxam™ 8400-7001
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3p2GX5_Maxxam-8400-7001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Specific Volume | 0.878 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Flexural Strength | 28.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 54.4 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 108CS20 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SLOVAMID® 6 NG GF 20 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Moplen HP400H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Yanshan PE LD160 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| LUVOCOM® 50-9310 | LEHVOSS Group | PC | LUVOCOM® |